Abstract
AbstractThe remarkable microstructural stability of high chromium steels prepared by powder metallurgy and strengthened by dispersion of nanometric yttrium oxides in cyclic loading at high temperatures is reported. Contrary to the continuous cyclic softening and profound changes in the microstructure during fatigue of common high chromium steels, the addition of 0.3 wt% Y2O3 stabilizes the microstructure and significantly reduces cyclic softening of investigated steels. The evolution of microstructure as a result of fatigue loading at room temperature, 650 and 750 °C, was examined by means of transmission electron microscopy. Only minor changes in the microstructure were detected. The stability of oxide particles after high‐temperature exposure was confirmed by energy dispersion spectroscopy chemical analysis. The microstructural features are discussed in relation to the cyclic behaviour of the oxide dispersion strengthened steels. The analysis of the hysteresis loop indicates that oxide nanoclusters are intersected and dissolved in slip bands of ODS Eurofer steel. This process contributes to cyclic softening.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Fatigue & Fracture of Engineering Materials & Structures
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.