Abstract
A three phase electromagnetic stirrer was used to agitate aluminum A356 slurry and a dry and oxygen free argon gas was introduced in to the slurry by a porous graphite core at a same time. The prepared semi-solid slurry was then transferred into a metallic mold and was compacted by a drop weight. Results demonstrated a favorable increase in shape factor, decrease in aspect ratio and average diameter size at different intensities of stirring. The intensity of stirring was changed by altering the current passed through the magnetic coil and also bubbling intensity via the porous graphite diffuser. Different time intervals for electromagnetic stirring and gas induction were applied. Agitating the slurry for 90 Sec. separately by electromagnetic stirrer and GISS method, gave better results in terms of shape factor, decrease in average diameter of the globules and aspect ratio.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.