Abstract
In this study, effects of 0.5, 1.0 and 1.5 mole% CuO addition on the properties of potassium sodium niobate (K 0.5Na 0.5)NbO 3-KNN ceramics were investigated. Pure KNN and CuO-added KNN pellet samples were sintered at 1100 and 1090 °C for 4 h, respectively. Phase analysis showed that all samples crystallized in pure orthorhombic perovskite phase. Addition of 1.0 and 1.5 mole% CuO caused grain growth, densification and formation of a liquid phase at the grain boundaries. Curie temperature has shifted from 480 to 435 °C with increasing CuO ratio. The most remarkable characteristic of the hysteresis loops were the constricted nature of the 0.5 mole% CuO-added KNN's curve and the antiferroelectric-like appearance of the 1.5 mole% CuO-added KNN's curve. Piezeoelectric properties of d 33 = 120 pC/N, k p = 0.27 and Q m = 772 were obtained from the 1.5 mole% CuO-added KNN.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.