Abstract
Molybdenum trioxide (MoO3) films, 15 µm thick, have been deposited on 50 µm thick polycrystalline titanium substrates from 250 to 500 °C via liquid spray pyrolysis. Molybdenum pentachloride (MoCl5) dissolved in methanol was used as the molybdenum source; ambient conditions provided the oxygen source. X-ray diffraction (XRD) data indicated that amorphous MoO3 films were produced at deposition temperatures below 400 °C. Randomly orientated polycrystalline MoO3 films were produced at 400 °C and higher deposition temperatures. The deposition temperature also influenced the surface area of the films and their average grain size. Subsequent conversion of the MoO3 films to high surface area (HSA) conductive films containing both γ–Mo2N and δ–MoN was accomplished via programmed reactions with anhydrous NH3 and involved the formation of MoO2 and MoOxN1−x as intermediate phases. The degree of crystallinity, surface area, and average grain size of the MoO3 films strongly influenced the average grain size and surface area of the resultant MoxN films.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.