Abstract
The microstructural evolution of AZ61 semi-solid magnesium alloy during semi-solid remelting process was studied in this paper. The semi-solid billet was fabricated by strain-induced melt activation (SIMA) method. The results showed that the initial semi-solid grains melt mainly through coalescence. With the prolongation of isothermal holding time, the grains grew up and spheroidized, in which the mean diameter of grain and liquid volume fraction increased. In the meantime, the higher the holding temperature, the faster the grain grew and spheroidized. The suitable reheating temperature of AZ61 semi-solid magnesium alloy was 592. The samples were susceptible to serious deformation beyond 597.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.