Microstructural evolution of super-clean reduced-activation martensitic steels irradiated with single-beam (Fe+) and sequential-beam (Fe+ plus He+) at 350°C and 550°C was studied. Sequential-beam irradiation induced smaller size and larger number density of precipitates compared to single-beam irradiation at 350°C. The largest size of cavities was observed after sequential-beam irradiation at 550°C. The segregation of Cr and W and depletion of Fe in carbides were observed, and the maximum depletion of Fe and enrichment of Cr occurred under irradiation at 350°C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.