Abstract
Under H2 atmosphere, the green strips were prepared from Al–5.8Zn–1.63Mg–2.22Cu–0.12Zr (mass fraction, %) powders by the semi-solid rolling process with a relative density from 76.1% to 88.0%. The role of temperature on microstructure and mechanical properties was investigated. With increasing rolling temperature from 580 to 610 °C, the disappearance of primary powder boundary and isolated pores, inter-diffusion of species and the change of grain boundary were accelerated. Moreover, the mechanism of microstructure evolution changes from the densification dominant regime to the coarsening dominant regime; the amount of η (MgZn2) phase decreased and more Al2Cu particles precipitated at grain boundaries. The optimum temperature for semi-solid rolling of Al–5.8Zn–1.63Mg–2.22Cu–0.12Zr powders was determined. The liquid fraction in the range of 53% to 67% corresponds with a high density level of green strips. The present experimental analysis suggests that semi-solid powder rolling can be optimized to manufacture strips with high mechanical properties.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Transactions of Nonferrous Metals Society of China
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.