Microstructural evolution in AZ91D magnesium alloy during electron beam welding

Abstract

Vacuum electron beam welding can have a low heat input, which means there is a minimum heat affected zone during welding of AZ91D magnesium alloy. From the observed microstructure, the weld of the AZ91D magnesium alloy can be divided into four regions, which are the weld metal zone, a partially-melted zone adjacent to the fusion boundary, a partially-melted zone adjacent to the base metal and the base metal zone. A sharp transition from the fusion zone to the non-melted zone, especially the characteristic partial melting microstructure and nature of the alloy elements, was observed. It was found that significant partial melting had taken place in the very narrow region around the weld metal of the AZ91D magnesium alloy. The Al content of eutectic β-Mg 17Al 12 in the partially-melted zone adjacent to the fusion boundary was close to the content in the continuously precipitated eutectic β particles in the fusion zone and much lower than the eutectic β in the base metal. The fully melted eutectic β-phase coexisted with the partially melted eutectic β phase in the partially-melted zone adjacent to the base metal.