Abstract
The microstructural evolution of A356 machining chips in the semisolid state was studied at different temperatures and holding times. The results showed that the elongated α-Al grains first recrystallized in the semisolid state and then became globular with a high shape factor (SF). Both the temperature and the holding time clearly affected the grain size and SF. When the heating temperature or holding time was increased, the grain size and SF gradually increased and finally became stable. Moreover, the Vickers hardness of primary α-Al grains gradually decreased with increasing heating temperature. The optimal slurry for semisolid processing, with a good combination of grain size and SF, was obtained when the chips were held at 600°C for 15 min. The semisolid slurry of A356 chips exhibited a lower coarsening rate of α-Al grains than those produced by most of the conventional semisolid processes. The coarsening coefficient was determined to be 436 μm3·s−1 on the basis of the linear Lifshitz–Slyozov–Wagner (LSW) relationship.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Minerals, Metallurgy, and Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.