Microstructural evolution and plastic stability during superplastic flow in a 7475 aluminium alloy

Abstract

Superplastic behaviour and microstructural evolution were examined at 788 K for strain rates in the range 2 × 10-4–2 × 10-3 s-1 in a 7475 aluminium alloy of nominal composition Al–(1·2–1·9)Cu–(5·2–6·2)Zn–(1· 9–2·6)Mg (wt-%). In addition, the variation of the strain hardening and plastic stability parameters with strain was investigated based on experimental grain growth and cavitation data. The strain hardening parameter at 2 × 10-4 s-1 was high over a wide range of strain because of the high grain growth rate. Decrease in the strain hardening parameter due to cavitation was negligible. The highest plastic stability parameter was attained at 2 × 10-4 s-1, although the strain rate sensitivity was the lowest for the strain rate range investigated. This demonstrates the influence of grain growth on high plastic stability during superplastic deformation.