Abstract
Wire arc additive manufacturing (WAAM) of Mg-RE (rare-earth)-Zn alloys is important for meeting the requirements of lightweight large-scale components with high manufacturing flexibility. The Mg-8.1Gd-2.6Y-0.7Zn-0.5Zr (GWZ831K, wt.%) alloys were fabricated through the use of WAAM technology, and the microstructure evolution along the building direction and corresponding mechanical properties were then studied. The as-built sample in this paper was composed of finely equiaxed ɑ-Mg grains, eutectic (Mg, Zn)3(Gd, Y) phase, cubic phase, and γʹ precipitates. Furthermore, due to the in-suit heat treatments that were induced by the multiple thermal cycles, more γʹ precipitates were observed in the middle region. The microstructures at different heights were characterized by alternatively distributed fine equiaxed grains (melt pool boundaries, MPB) and coarse equiaxed grains (melt pools, MP). The mechanical properties of the as-built component were found to exhibit yield strength (YS), ultimate tensile strength (UTS), and elongation (EL) of 159 ± 1.0 MPa, 237 ± 4.0 MPa, and 6.7 ± 0.4 % in the building direction (BD) and 163 ± 5.1 MPa, 242 ± 8.7 MPa, and 7.0 ± 0.7 % in the traveling direction (TD). This demonstrates that the WAAM-processed GWZ831K alloy has good isotropy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.