Abstract
Cu/Nb multilayer composites with minimum individual layer thicknesses of ≈2.8 μm are achieved by accumulative roll bonding (ARB). The microstructural evolution and mechanical properties of these composites are investigated with different layer thicknesses after ARB processing. The results show that there is no visible interfacial reaction between the Cu and Nb layers, and the kernel average misorientation (KAM) distributions in electron backscatter diffraction (EBSD) maps remain in steady state during the third to seventh ARB cycles. The tensile testing results demonstrate that the yield strength increases with decreasing layer thickness in Cu/Nb multilayer composites. A simultaneous increase of strength and elongation is achieved by regulating the laminated structures. Microstructure and fracture analysis indicate that the simultaneous increase of strength and elongation is attributable to the high density of bimetal interfaces, which act as a barrier for dislocation mobility and crack propagation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.