Abstract
The most relevant range of compositions of Zn–Sn high-temperature solder alloys remains between 10 and 40 wt%Sn. Hence, transient directional solidification experiments have been carried out with Zn–10, 20, 30 and 40wt%Sn alloys under a wide range of cooling rates (T˙) with a view to investigating the corresponding microstructural evolution. The microstructure is shown to be formed mainly by an alternation of Zn-rich plate-like cells and a eutectic mixture. Morphological instabilities of the Zn-rich plates are shown to start for the lower content Zn–10 and 20wt%Sn alloys, however a microstructural transition of these plates into cylindrical-type horizontal cells can only be found in the microstructure of the 30 and 40wt%Sn alloys. Experimental growth laws are proposed relating the microstructural spacing (λ) to solidification thermal parameters. Hardness (HV) is shown be affected by both the positive segregation of Sn, the alloy volumetric fraction of Zn and λ. Hall-Petch type equations are proposed relating HV to λ.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.