Abstract
Gas‐pressure sintering of α‐Si3N4 was carried out at 1850 ° to 2000°C in 980‐kPa N2. The diameters and aspect ratios of hexagonal grains in the sintered materials were measured on polished and etched surfaces. The materials have a bimodal distribution of grain diameters. The average aspect ratio in the materials from α‐Si3N4 powder was similar to that in the materials from β‐Si3N4 powder. The aspect ratio of large and elongated grains was larger than that of the average for all grains. The development of elongated grains was related to the formation of large nuclei during the α‐to‐β phase transformation. The fracture toughness of gaspressure‐sintered materials was not related to the α content in the starting powder or the aspect ratio of the grains, but to the diameter of the large grains. Crack bridging was the main toughening mechanism in gas‐pressure‐sintered Si3N4 ceramics.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.