Abstract
Abstract The effects of laser nitriding on the microstructural evolution and wear and corrosion behaviors of the NAK80 mold steel (AISI P21) were investigated. A high-power diode laser with a laser energy density of 1125 J/mm2 was employed for laser nitriding of NAK80. To examine the microstructure of laser-nitrided NAK80, diverse characterization methods such as scanning electron microscopy with electron backscatter diffractometry, high-resolution transmission electron microscopy with electron energy loss spectrometry, and atom probe tomography were utilized. These analyses revealed that the laser-nitrided region consisted of rod-like aluminum nitride (AlN) precipitates with various nitrides and carbides in the martensite matrix, resulting in the surface hardening of NAK80 from 409 to 536 HV. As a result, the laser-nitrided NAK80 exhibited an enhancement in the wear resistance in comparison to that of the base metal in the fretting test. The wear loss of laser-nitrided NAK80 was reduced by 33.4% compared to that of the base metal after 40,000 fretting cycles. However, a deterioration in the corrosion resistance was observed for the laser-nitrided NAK80 compared to the base metal. It may be associated with the elemental segregation in the vicinity of the AlN precipitates, which was observed in the atom-probe tomography.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.