Abstract
The aim of this research was to apply a protective composite coating made of ultra-high temperature ceramics (UHTCs) on the graphite substrates. The spark plasma sintering (SPS) method was used to apply this coating on the graphite substrate. First, efforts were made to choose the right chemical composition for the composite material of the coating and the sintering conditions (temperature, pressure, and holding time) for applying the coating. Then, single-layer coatings with the basic composition of ZrB2–SiC–Si with WC and MoSi2 additives in equal amounts of 1.25 and 3.75 vol% of each were successfully applied on the graphite substrates under sintering conditions of 1875±25 °C final temperature, 10 MPa initial pressure, 25 MPa final pressure and 5 min holding time. The presence of the Si element in the basic composition of these coatings, in addition to helping to form an intermediate diffusion layer at the interface between the composite coating and the graphite substrate, caused the strengthening of the joining despite the difference in the coefficient of thermal expansion between the graphite and the composite coating.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.