Abstract
Characterization of microstructure of silicide coatings obtained during diffusion process of pack cementation type was showed in this article. The basic materials were pure Mo sheet and TZM molybdenum alloys as well. The coatings were deposited in out of pack process with three different times of exposure. The temperature of deposition process was constant. In first step the phases compositions of coatings was described by XRD analysis. In each cases the MoSi2 phase was obtained on top surface of the coatings. The morphology of the coatings was very similar as well. All types of coatings were characterized by network of cracks on top surface of the coatings. There was no influence of depositions time on phases constituent and coatings topography. LM and SEM analysis revealed that internal coatings morphology was very similar in all cases. Basic differences was related to the thickness of coatings. All coatings were good quality without deep cracks. Microstructure was a columnar-like type without pores and voids.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.