Abstract
Microstructures of switch-back epitaxy cubic silicon carbide (3C-SiC) before and after Al ion implantation were investigated by transmission electron microscopy (TEM). Stacking faults aligned along the {111} were observed in 3C-SiC. A surface bulge was observed in some regions and planar defects were observed under the bulge region. After ion implantation of 3C-SiC, defects were observed to be distributed up to a depth approximately 500 nm from the surface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.