Abstract
In this work, transmission electron microscopy has been used to investigate HgCdSe/ZnTe/Si (211) heterostructures grown by molecular beam epitaxy and to study the effects of chemical etchants for measurements of defect density in the HgCdSe epilayers. Both ZnTe/Si and HgCdSe/ZnTe interfaces were decorated with {111}-type stacking faults inclined at angles of ∼ 19° or ∼ 90° with respect to the interface plane. Similar stacking faults were also present in the upper regions of the HgCdSe films. High-resolution imaging and Fourier image analysis revealed dislocations, mostly with $$ \frac{a}{3}\left\langle\bar{1}11\right\rangle $$ Burgers vector, at both ZnTe/Si and HgCdSe/ZnTe interfaces. Etching solutions based on different combinations of nitric acid, hydrochloric acid and lactic acid were tried in attempts to identify an etchant that provided one-to-one correspondence between etch pits and defects in the HgCdSe layer. Focused-ion-beam milling and transmission electron microscopy were used to prepare site-specific cross-section samples from across the etch pits. However, many defects in regions surrounding the etch pits were unaffected by the various different etchants.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.