Abstract
Abstract This study involves the effect of boriding powder composition on the microstructure and hardness of a CoCrMo alloy borided in a solid medium using the powder pack method. To investigate the effect of boriding powder composition, two different commercial boriding agents, Ekabor-HM and Ekabor III, were thoroughly mixed with ferrosilicon powders to form the boriding media. The CoCrMo samples were tightly packed with the Ekabor-HM and Ekabor III boriding powders in stainless steel containers to minimize oxidation. The boriding process was carried out under atmospheric conditions for 9 h in an electrical resistance furnace preheated to 1223 K. X-ray diffraction (XRD) analyses revealed that the surfaces of the borided CoCrMo alloys consisted of a bilayer composed of CoB and Co2B phases and also contained minor amounts of CrB, Mo2B5, and Mo2B. The average thickness of the boride layer in the samples borided with Ekabor HM and Ekabor III powders was 28±4.1 μm and 21±2.3 μm, while the average hardness of the boride layer was 1752±5.3 HV0.1 and 1364±3.8 HV0.1, respectively.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.