Abstract
Alloys with superior properties represent the main topic of recent studies due to their effectiveness in reducing the cost of equipment maintenance and enhancing usage time, in addition to other benefits in domains such as geothermal, marine, and airspace. Al0.5CrFeNiTi was produced by solid state processing in a planetary ball mill, with the objective of obtaining a high alloying degree and a homogenous composition that could be further processed by pressing and sintering. The metallic powder was technologically characterized, indicating a particle size reduction following mechanical alloying processing when compared to the elemental raw powder materials. The microstructural analysis presented the evolution of the alloying degree during milling but also a compact structure with no major defects in the pressed and sintered bulk samples. The X-ray diffraction results confirmed the presence of face-centered cubic (FCC) and body-centered cubic (BCC) phases, predicted by the theoretical calculations, along with a hexagonal close-packed (HCP) phase, where the Al, Cr, Fe, Ni, and Ti phase was identified in both the alloyed powder material and sintered sample.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.