Abstract
Static indentation and uniaxial compression tests have been conducted on Armox500T steel and its weldments to predict the constraint factor (CF), i.e., ratio of Meyer’s hardness to uniaxial flow stress. Series of dynamic indentation experiments were carried out at impact velocities ranging from 5 to 300 m/s to estimate dynamic hardness as a function of average strain. Subsequently, dynamic indentation (DI) test data and CF determined under static indentation conditions have been used to study the high strain rate plastic flow behavior of Armox500T weldments in comparison with the base metal. It was observed that flow stress for Armox500T and its weldments under dynamic loading conditions (104 s−1) are significantly higher than flow stress measured under static loading conditions (10−3 s−1). The plastic flow behavior computed from DI is in good agreement with the data evaluated through conventional split Hopkinson pressure bar technique. Further, the study of the microstructure of base metal and weldments by optical microscopy and SEM revealed a considerable variation in the microstructure.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.