Abstract The effect of powder size on the microstructure and mechanical properties was studied in gas-atomized Al-14wt%Ni-14wt%Mm (Mm: misch metal) alloy powder and their extrudates. The alloy powders showed different microstructures depending on the powder size. With decreasing powder size, formation of intermetallic compounds such as Al 3 Ni, Al 11 Ce 3 and Al 11 La 3 was suppressed. The powders less than 26 μm in diameter consisted of nanocrystalline fcc-Al particles embedded in an amorphous matrix. Microstructural scale of the extruded bar decreased as the initial powder size was decreased. The ultimate tensile strength of the alloy bar has increased from about 512 to 728 MPa with decreasing initial powder size from 75 to 90 μm to −26 μm. The strength increase mainly results from structural refinement.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.