Microstructural Aspects of Infiltration Growth YBCO Bulks With Chemical Pinning

Abstract

Single grain YBa <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> Cu <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">7-x</sub> (YBCO, Y123) bulk superconductors were prepared by the infiltration growth process. The solid phase precursor was prepared by solid-state synthesis from Y <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> +BaCuO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> powders. The influence of the composition of the source of melt for infiltration and the CeO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> addition on the transition temperature and critical current density was studied. It is shown that the studied samples are doped by Yb from the Yb <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> substrate. The dependences of Yb concentration on the distance from the bottom of the samples were measured by the energy dispersive spectroscopy microanalysis at a scanning electron microscope. Correlation between the fabrication technology, level of Yb doping, microstructure, and superconducting properties is discussed.