Abstract
The present work concerns the processing of 7075 Al alloy by cold compaction and hot extrusion of a premixed powder. To this end, a premixed Al–Zn–Mg–Cu powder, Alumix 431D, was uniaxially cold pressed at 600MPa into cylindrical compacts 25mm in diameter and 15mm thick. Subsequently, selected green compacts were subjected to either a delubrication or presintering heat treatment. Extrusion of the powder compacts was performed at 425°C using an extrusion ratio of 25:1. No porosity was present in the microstructures of the extruded alloys. Heat treatment prior to extrusion had a great effect on the degree of alloy development in powder compacts and, as a direct consequence, remarkably affected the extrusion process and the as-extruded microstructures and mechanical properties of the processed materials. Hot extrusion caused banded structures for the alloys consolidated from the green and delubricated powder compacts. The alloy extruded from the presintered powder compact showed a fine, recrystallized microstructure which resulted in a superior combination of mechanical properties for the consolidated material.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.