Abstract
Nanostructured Al-9%Si-3%Cu alloy was achieved by direct metal laser sintering (DMLS) and then processed using high-pressure torsion (HPT) processing, which resulted in considerable grain refinement down to 60 nm associated with a substantial dislocation density up 6.2 × 1014 m−2 and a significant reduction in the porosity. Hardness measurements across the horizontal and vertical cross sections showed an improvement in the strength homogeneity for processed samples after 10 turns of HPT processing. These results indicate that a controllable ultrafine-grained microstructure can be achieved by employing additive manufacturing, followed by effective severe plastic deformation processing.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.