Abstract
After prolonged cyclic stressing in rolling contact, AISI 52100 bearing steel parts develop extensive regions of microstructural alteration, designated as white etching areas. These are oriented in predictable directions relative to the rolling track. Lenticular carbides are always associated with these areas. Evidence is presented indicating that the boundaries of lenticular carbides constitute planes of weakness which may be preferred planes of fatigue cracking. In the transmission electron microscope the martensitic structure appears gradually transformed into a cell like structure by the action of cyclic stress. The size of crystallites is greatly reduced in this process. The density of microstructural change is found increased with cycling and is distributed in depth along a curve resembling that of the calculated maximum unidirectional shear stress with little or no visible change in the region of maximum orthogonal (alternating) shear stress.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.