Microscopic structure and properties of wood-based foaming composites

Abstract

In order to reduce the density of wood-based composites without causing a deterioration of their mechanical properties, we studied the process of manufacturing wood-based composites. A combination of polymer foaming technology and flat hot-pressing technology was used. The microscopic structure of the various wood-based composites was analyzed with a scanning electron microscope (SEM). Modulus of rupture (MOR), modulus of elasticity (MOE), impact strength, and thickness expansion rate of water sorption (TS) were all measured. The results showed that fibers loosely interweave, and fibers had been connected by micropore. They also showed that spaces between fibers had big micropore structure. MOR, MOE and impact strength were the highest among three levels of ratio. When the total content of resin and foaming agent were 20% by weight, TS was higher. A hot-pressing temperature of 120°C was optimal. At the low temperatures of 80°C, the foaming process was uncompleted. At a higher temperature, micropores burst at a certain pressure. Based on the variance analysis and maximum difference analysis, a significance test shows that the optimum conditions for the total content of resin and foaming agent is 20% by weight, with a hot pressing temperature of 120°C for 15 min. Under these conditions, the properties of wood-based foaming composites all achieved the industry standard.