Abstract
In this study, damage mechanisms in AA5182-O aluminium sheets are investigated using quasi-static (QS) Marciniak tests and high strain-rate electro-hydraulic forming (EHF) process. The results confirm that void nucleation, growth and coalescence are the main damage mechanisms of AA5182-O at both high and low strain rates. The EDS analysis suggests that cracking of Al3(Fe-Mn) intermetallic particles is the main source of void nucleation, whereas Mg2Si particles do not majorly influence void formation. Void growth analysis suggests that specimens deformed under QS conditions contained more voids in areas away from the sub-fracture surface but specimens deformed at high strain rate exhibit more significant rate of void growth close to sub-fracture areas. Void formation is suppressed by increasing the applied energy in EHF. And more significantly, the growth of voids is suppressed due to the high-velocity impact of the sheet against the die which plays an important role in increasing formability of AA5182-O aluminium sheet in EHF process. When the void percentage increase remains less than about 0.5% AA5182-O can be formed safely. However, when the void percentage increases beyond 0.6–0.8% fracture becomes inevitable.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.