Abstract
In this study, pitch crosslinked by oxygen function groups was made into activated carbon (AC) and pore structure was observed. The oxygen functional groups were introduced by the addition of waste PET for pitch synthesis. Activation agent ratios used to obtain the AC during the activation process were 1:1, 1:2 and 1:4 (pitch:KOH, w/w). The oxygen content in the prepared pitch was characterized by elemental analysis. Also, the molecular weight of pitch was investigated by MALDI-TOF. Specific surface area and micropore volume of the prepared AC were determined by the argon adsorption–desorption analysis and calculated using the Brunauer–Emmett–Teller and Horvath–Kawazoe equations, respectively. Micropore fraction of PET-free AC was smaller than that of PET-added AC. At high activation agent ratio, mesopores were created when the micropore structure collapsed. However, in the PET-added AC, due to the oxygen crosslinking effect, the micropore structure and micropore size were maintained even at a high activation agent ratio. Therefore, PET AC was found to have a higher micropore fraction than that of PET-free AC.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.