Abstract
In JET with ITER-like wall, beryllium eroded in the main chamber is transported to the divertor and deposited mainly at the horizontal surfaces of tiles 1 and 0 (high field gap closure, HFGC). These surfaces are tungsten coated carbon fibre composite (CFC). Surface sampleswere collected following the plasma operations in 2011–2012 and 2013–2014 respectively. The surfaces, as well as polished cross sections of the deposited layers at the surfaces have been studied with micro ion beam analysis methods (µ-IBA).Deposition of Beand other impurities, and retention of D is microscopically inhomogeneous. Impurities and trapped deuterium accumulate preferentially in cracks, pits and depressed regions, and at the sides of large pits in the substrate (e.g. arc tracks where the W coating has been removed). With careful overlaying of µ-NRA elemental maps with optical microscopy images, it is possible to separate surface roughness effects from depth profiles at microscopically flat surface regions.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.