Abstract
This paper describes the micro-patterning of thick NdFeB magnetic films using a high-power plasma etching method. The effects of RF bias power and gas composition on the selectivity and etching rate are experimentally studied. A maximum etching rate of 60 nm min−1 is achieved with an inductively coupled plasma power of 500 W and a RF bias power of 200 W. A maximum selectivity of 0.26 between hard baked AZP4903 photoresist and NdFeB magnetic films is achieved when volumetric Cl2 concentration is 2.5%. NdFeB micro-magnets as thick as 4.2 µm are achieved by using AZP4903 photoresist. Magnetic film as thick as 10 µm can be patterned by using SU-8 photoresist with a thickness of 100 µm as the mask. The magnetic property of patterned microstructures is characterized using a vibrating sample magnetometer and the magnetic field distribution is measured using a Hall effect sensor IC. The characterization results indicate that the patterned magnetic microstructures have a high magnetic remanance of 1.0 T, which is comparable to that of the non-patterned NdFeB films.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.