Morphology control of poly( p-phenylene pyromelliteimide) (PPPI) crystals was examined using reaction-induced crystallization of oligomers during solution polymerization of self-polymerizable N-(4′-aminophenyl)-3-carboxyl-4-alkoxycarbonylphthalimide. Micro-flowers of the PPPI needle-like crystals were formed in which the needle-like crystals grew radially from the center part as petals. The molecules aligned regularly along the long axis of the needle-like crystal. The structure of alkoxy group in the monomer and the monomer concentration influenced the size of the needle-like crystals, and their average length and width were changeable from 640 nm to 1.69 μm and from 110 nm to 210 nm, respectively. The average thickness was 20 nm. The obtained micro-flowers possessed high crystallinity and exhibited excellent thermal stability.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.