Abstract
This is a study of the micro- and macrostructural variations in samples of stainless steel with the overall composition of the grade 316L, produced using electron beam melting. Electron beam melting is one of the processing methods under consideration for manufacturing some of the International Thermo- Nuclear Experimental Reactor In-Vessel components. Therefore further studies of the homogeneity of the material were conducted. Electron beam melting results in a complicated thermal history of the manufactured part giving a significant impact on the microstructure. A cellular structure that is often observed in samples prepared by selective laser melting was found in the top layers of the specimens. Further down, the structure changed until the cellular structure was almost non-existing, and the grain boundaries had become more pronounced. This revelation of a heterogeneous structure throughout the entire part is crucial for large-scale industrial applications like the Thermo- Nuclear Experimental Reactor to make sure that it is understood that the properties of the material might not be the same at every point, as well as to assure that the correct post-treatment is done. It is also exposed that a significant part of this change is due to molybdenum redistribution inside the sample when it diffuses from the cell boundaries into the cells, and into bigger agglomerates in the grain boundaries. This diffusion seems not to affect the microhardness of the samples.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.