Surface tensions of MgCl2-KCl and KNO3-NaNO3 binary melts have been measured by means of the maximum bubble pressure method over the temperature ranges of 650∼875°C and 270∼405°C respectively.The variation of the constituent ionic species with composition for the MgCl2-KCl binary system has been estimated by comparing the results obtained with those determined for the KNO3-NaNO3 binary system having relatively strong ionic characters. The results obtained are summarized as follows:(1) For both systems, the surface tension shows an approximately linear decrement with increasing temperature at each composition. The surface tension and its temperature coefficient of molten MgCl2 are considerably low as compared with those of other chlorides but these are markedly increased by the addition of KCl. These trends are considered to be indicating the associating property as in the case of molten ZnCl2 previously studied by the authors.(2) The variation of the surface tension at the melting point with composition is well corresponding to the phase diagram for the KNO3-NaNO3 system, but not for the MgCl2-KCl system, particularly on the MgCl2-rich side. The temperature coefficient of surface tension corresponding to the surface entropy per unit area and the surface enthalpy per unit area vary monotonously with composition in the KNO3-NaNO3 system, but show notable inflections at about 30 and 80 mol%KCl in the MgCl2-KCl system. The surface heat of mixing per unit area for the MgCl2-KCl system shows a maximum and a minimum at about 30 and 90 mol%KCl.(3) The surface tensions calculated from a modified Guggenheim equation agreed very well with the experimental values for KNO3-NaNO3 binary melts, indicating that this system can be treated as a nearly ideal solution.(4) It is also found that the variations of the surface properties with composition are well corresponding to the changes of the other physicochemical properties in the MgCl2-KCl system.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of the Japan Institute of Metals and Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.