Abstract
Porous OSG low-k dielectrics deposited by using TEOS and MTEOS mixture with different ratios and Brij® 30 surfactant. The deposited samples contain a different concentration of terminal methyl groups that is proportional to MTEOS concentration. An increase in the methyl groups concentration by changing TEOS/MTEOS ratio decreases the open porosity, k-value, and Young’s modulus and increases the mean pore radius although the template concentration was kept constant. Plasma damage by fluorine radicals depends on the carbon concentration in the films. It can be reduced by 60% when the carbon concentration in the film exceeds 10 atomic percent as measured by XPS (the films deposited with TEOS/MTEOS ratio 40/60).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.