Abstract
: A new method for transmission electron microscope (TEM) specimen preparation using a focused ion beam (FIB) system that results in a lower rate of gallium (Ga) implantation has been developed. The method was applied to structural and analytical studies of composite materials such as silicon (Si)-devices and magneto-optical disk. To protect the specimens against Ga ion irradiation, amorphous tungsten (W) was deposited on the surface of the specimen prior to FIB milling. The deposition was quite effective in reducing the Ga implantation rate, and energy-dispersive X-ray (EDX) analysis of these specimens detected 0.3-1.5% Ga incorporated in the thinned area. FIB milling times for these specimens were 1.5-2 hr, with a starting thickness of about 50 µm. Although the milling rate was high, all the materials were properly prepared for TEM study, and clear crystal lattice images were observed on all specimens.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Microscopy and microanalysis : the official journal of Microscopy Society of America, Microbeam Analysis Society, Microscopical Society of Canada
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.