Methane steam reforming for producing hydrogen in an atmospheric-pressure microwave plasma reactor

Abstract

A methane steam reforming process for producing mainly hydrogen in an atmospheric-pressure microwave plasma reactor is demonstrated. Nano carbon powders, CO x , C 2H 2, C 2H 4, and HCN were also formed. Intermediates such as OH, NH, CH, and active N 2 were identified using optical emission spectroscopy. The selectivity of H 2 was greater than 92.7% at inlet H 2O/CH 4 molar ratio ( R) ≧ 0.5, and was higher than that obtained using methane plasmalysis because steam inhibited the formation of C 2H 2. The highest methane conversion was obtained at R = 1, reaching 91.6%, with the lowest specific energy consumption of H 2 formation at [CH 4] in = 5%, 1.0 kW, and 12 slpm. The plasma-assisted catalysis process, which packed Ni/Al 2O 3 catalysts in the discharge zone and supplied heat using hot effluents, was used to elevate the methane conversion and hydrogen selectivity. However, large amounts of 40–70 nm carbon powder, which is electrically conductive, were produced, resulting in rapid catalyst deactivation due to carbon being deposited on the surface and in the pores of catalysts.