Abstract
In this paper, the influence of impact and incendiary effect on the microstructure changes and crack development in non-homogenous add-on armour is studied. The main objective was to determine the parameters that may cause the yielding of the material, leading to a possible decrease in multi-hit resistance. For that purpose, patented wire fence and perforated plates made from two types of high strength steel, Hardox 450 and 50CrV4 tempered at 170 °C were tested. Various techniques were applied: high speed video camera was used, visual macroanalysis, light microscopy, scanning electron microscopy and energy dispersive X-ray analysis. It was found that incendiary effect, being of a brief nature, does not have any influence on microstructure of the add-on armour. However, impact greatly influences crack development and propagation, which occurs in 50CrV4 steel, the material with lower ductility, diminishing its multi-hit resistance. In accordance with obtained results, non-homogenous add-on armour behaviour models were devised, describing the influence of material ductility and geometry on fracture mode, stresses and deformability.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.