AbstractAqueous zinc batteries usher in a renaissance due to their intrinsic security and cost effectiveness, bespeaking vast application foreground for large‐scale energy storage system. However, uncontrolled dendrite growth along with hydrogen evolution severely restricts its reversibility and stability for practical application. Herein, the surface of Zn metal is reconstructed with metallic particles (In, Sn, In0.2Sn0.8) to diminish surface defects and regulate Zn deposition behavior. The alloyed In–Sn greatly activates the Zn surface for lower Zn adsorption energy barrier to expedite plating kinetics and confine Zn aggregation. Dense and uniform deposition of Zn on the reconstructed surface significantly prevents the Zn substrate from dendrites growth for catastrophic damage. Meanwhile, alloy layer embodies high hydrogen evolution overpotential, ensuring high plating and stripping efficiency for Zn anode. Consequently, In0.2Sn0.8 reconstructed surface realizes long‐term lifespan up to 1800 h with low polarization (12 mV) at the condition of 1 mA cm−2 and 1 mAh cm−2. When paired with sodium vanadate (NVO) cathode, the full cell steady operates for a high‐capacity retention of 94.0% after 5000 cycles at 5 A g−1. This study provides new insights into the surface‐defects dependent Zn deposition process and offers a guide for constructing stable surface for dendrite‐free Zn growth.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.