Abstract
Metal-assisted etching of silicon in HF/H 2O 2/H 2O solutions with Ag nanoparticles as catalyst agents was investigated. SEM observations and etch rate measurements were carried out as a function of the etching solution composition. Depending on the relative amount of HF and H 2O 2, different regimes of dissolution take place and a strong similarity with the etching in HF–HNO 3 solution is evidenced, for the first time. Formation of meso- and macroporous Si, etched craters and polished Si are observed as the HF/H 2O 2 ratio decreases. The dissolution mechanisms are discussed on the basis of a localized hole injection from the Ag nanoparticles into Si and in terms of the well known chemistry of Si dissolution in HF-based chemical and electrochemical systems. At high HF/H 2O 2 ratio, there is no formation of oxide at the surface. Hole injection and Si dissolution occur at the level of the Ag nanoparticle only, resulting in the formation of meso and macropores depending on the Ag nanoparticle size. At low HF/H 2O 2 ratio, the Si surface is oxidized, the injected holes are homogeneously distributed and thus polishing occurs. There is an intermediate range of composition in which injected holes diffuse away from the Ag nanoparticles and cone-shaped macropores, several tens of nm in diameter are formed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.