Abstract
Mesoporous TiO2 nanoparticles were synthesized with the hydrothermal method and characterized by powder X-ray diffraction (PXRD) and transmission electron microscope (TEM). Then a superior solid-phase microextraction (SPME) fiber was fabricated by sequentially coating the stainless steel fiber with silicone sealant film and mesoporous TiO2 powder. The developed fiber possessed a homogeneous surface and a long life-span up to 100 times at direct immersing (DI) extraction mode. Under the optimized conditions, the extraction efficiencies of the self-made 17μm TiO2 fiber for six organochlorine pesticides (OCPs) were higher than those of the two commercial fibers (65μm PDMS/DVB and 85μm PA fibers) which were much thicker than the former. As for analytical performance, low detection limits (0.08–0.60ngL−1) and wide linearity (5–5000ngL−1) were achieved under the optimal conditions. The repeatabilities (n=5) for single fiber were between 2.8 and 12.3%, while the reproducibilities (n=3) of fiber-to-fiber were in the range of 3.7–15.7%. The proposed fiber was successfully applied to the sensitive analysis of OCPs in real water samples and four of the six analytes were detected from the rainwater and the lake water samples.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.