Melt-spun bio-based PLA-co-PET copolyester fibers with tunable properties: Synergistic effects of chemical structure and drawing process

Abstract

The fabrication of bio-based copolyester fiber with adjustable crystallization, orientation structure and mechanical property still remains a great challenge. In this study, a series of copolyester fibers based on terephthalic acid (PTA), ethylene glycol (EG) and l-Lactide (L-LA) were prepared via melt copolymerization and spinning. The resultant PLA-co-PET (PETLA) fibers exhibited tunable structure and property due to the synergistic effects of chemical structure and drawing process. The chemical structure of PETLA was confirmed by NMR, FTIR and XRD, which suggested that the random degree of copolymer increased with LA content and the viscosity decreased with the increase of LA content. The crystallization behavior, melting characteristic, thermal stability and rheological property were investigated by DSC, TGA and rheometer, the results indicated that all the PETLA exhibited the crystallization capacity, melting temperature and thermal stability were slightly affected by LA segment. The synergistic effects of LA segment and spinning process on PETLA structure and property were analyzed by WAXD and SAXS. The breaking strength of PETLA fibers dropped from 5.3 cN/dtex of PET to 2.8 cN/dtex of PET85LA15, which still met the requirements of most textile applications. Therefore, our work presented a feasible approach to prepare bio-based polyester fibers with tunable property.