Abstract
Melting, solidification, and viscosity properties of multicomponent Fe-Cu-Nb-Mo-Si-B alloys with low aluminum addition (up to 0.42 at.% Al) were studied using an oscillating cup viscometer. It is shown that melting and solidification are divided into two stages with a knee point at 1461 K. The temperature dependences of the liquid fraction between the liquidus and solidus temperatures during melting and solidification are calculated. It has been proven that aluminum accelerates the processes of melting and solidification and leads to an increase in liquidus and solidus temperatures. In the liquid state at temperatures above 1700 K in an alloy with a low aluminum content, the activation energy of viscous flow increases. This growth was associated with the liquid-liquid structure transition, caused by the formation of large clusters based on the metastable Fe23B6 phase. Aluminum atoms attract iron and boron atoms and contribute to the formation of clusters based on the Fe2AlB2 phase and metastable phases of a higher order.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.