Abstract
Melting of original crystals and their recrystallization during heating were successfully separated for isothermally crystallized poly(butylene terephthalate) (PBT). The corresponding kinetics was determined and quantitatively discussed for a wide range of heating rates (0.1–100,000 K s-1) using fast-scanning chip calorimetry (FSC) and differential scanning calorimetry (DSC). The double melting peaks observed on the FSC curves are assigned to the melting of original crystals (low-temperature peak) and recrystallized and/or reorganized crystals (high-temperature peak). Heating rate dependence of the degree of recrystallization has been evaluated and the kinetics was discussed on the basis of Ozawa's method. Compared with the melt-crystallization and cold-crystallization, recrystallization kinetics is the fastest process. This is because many crystal remnants, which do not transform into the isotropic melt, act as athermal nuclei, and accelerate recrystallization.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.