Melt-extruded guides for peripheral nerve repair based on poly(epsilon-caprolactone) (PCL) were realised and their physico-chemical properties were evaluated. Preliminarily, PCL cast films were found to support the attachment and proliferation of Neonatal Olfactory Bulb Ensheating Cells (NOBEC). S5Y5 neuroblastoma cells were cultured inside PCL guides in their uncoated form or coated with a non-specific adhesion protein (gelatin) and a specific peptide for nerve regeneration (poly(L-lysine)). Coating increased cell density (gelatin) and/or the cell density rate on substrates (poly(L-lysine); gelatin) as compared to uncoated guides. Various in vivo tests were carried out for the repair of small (0.5 cm), medium (1.5 cm) and long (4.5 cm) size defects in the peripheral nerves of Wistar rats. For the small nerve defects, uncoated and coated PCL guides were tested. Results from in vivo tests were subjected to histological examination after 45 days, 6 and 8 months postoperative for small, medium and large defects, respectively. Regeneration was found for small and medium size defects. For 0.5 cm defects, the coating did not affect regeneration significantly. Grip-tests also evidenced functional recovery for the 1.5 cm-long defects treated with PCL guides, after 6 months from implantation. On the other hand, mechanical stiffness of PCL conduits impaired the repair of 4.5 cm-long defects in 8-month period: the lack of flexibility of the guide to rat movements caused its detachment from the implant site. The research showed that PCL guides can be used for the successful repair of small and medium size nerve defects, with possible improvements by suitable bio-mimetic coatings.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.