Abstract
This preliminary study aims to clarify how Co, TaCr2 and TiB2 grain refinement inducing inoculants influence the melt pool physics and resulting grain structure in superalloy IN718 processed by laser powder bed fusion (L-PBF). It was demonstrated that the presence of solid inoculant particles could affect the melt pool convection leading to a noticeable reduction in the melt pool width and penetration depth as well as the balling phenomenon. Interestingly, it was found that the penetration depth of the melt pool in samples containing TiB2 appeared to be unchanged due to the presence of nano-particles. Characterization of the resulting grain structures of the various samples revealed that the difference in melt pool geometries contributed to a predominant columnar-grained structure with< 101 > texture in samples containing Co or TaCr2 inoculants while an equiaxed-grained structure with< 001 > texture in samples containing TiB2 inoculants. The effectiveness of inoculants was found to be closely related to their impact on the melt pool physics, in addition to the degree of lattice disregistry with the IN718 matrix.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.