Production of biocompatible composite scaffolds shifts towards additive manufacturing where thermoplastic biodegradable polymers such as poly(lactic acid) (PLA) are used as matrices. Differences between industrial- and medical-grade polymers are often overlooked although they may affect properties and degradation behaviour as significantly as the filler addition. In the present research, composite films based on medical-grade PLA and biogenic hydroxyapatite (HAp) with 0, 10, and 20 wt.% of HAp were prepared by solvent casting technique. The degradation of composites incubated in phosphate-buffered saline solution (PBS) at 37 °C after 10 weeks showed that the higher HAp content slowed down the hydrolytic PLA degradation and improved its thermal stability. Morphological nonuniformity after degradation was indicated by the different glass transition temperatures (Tg) throughout the film. The Tg of the inner part of the sample decreased significantly faster compared with the outer part. The decrease was observed prior to the weight loss of composite samples.
Published Version (
Free)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.