Abstract
A detailed analysis of the microstructure and failure mechanism of a dual-phase steel material as a function of strain was conducted. Accordingly, three tensile tests were performed and interrupted at different strain levels in order to investigate void nucleation, void growth and void coalescence. Scanning electron microscopy analysis revealed that void nucleation occurs by ferrite grain-boundary decohesion in the neighborhood of martensite grains. Further, void initiation could be observed between closely situated martensite grains. Martensite morphology and distribution has a significant impact on the accumulation of damage. The mechanism of failure was found to be influenced by deformation localization due to microstructural inhomogeneity. Based on the experimental observations and simulation results, a model describing the failure mechanism is proposed for dual-phase steel material.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.