Abstract
Ceria removal during the STI post-CMP cleaning process has recently become a serious concern in the semiconductor industry. Understanding ceria adhesion and its removal mechanism is necessary for designing a suitable post CMP cleaning methodology. Recently, colloidal ceria slurries have been heavily used due to the low defectivity factor. In this work, colloidal ceria adhesion and removal behaviors were studied as a function of particle sizes. It was found that polishing produces more contamination of ceria to oxide surface than dipping conditions and the strength of adhesion is increased with decreasing ceria size due to a higher Ce3+ concentration for smaller size particles resulting in more Ce-O-Si bonding. Ceria adhesion is mainly attributed to Ce-O-Si bond formation. Different cleaning methods (megasonic, brush scrubbing, SC1 (standard cleaning solution 1), DHF (diluted hydrofluoric acid) and SPM (sulfuric acid and hydrogen peroxide solution) were employed in removing these ceria particles. It was found that larger particles could be removed effectively with physical force, and smaller particles could be removed using chemicals such as DHF or SPM. Hence, it is concluded that an appropriate cleaning method should be chosen based on the size of the ceria.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.